Technical datasheet for PPS 804 GM6 material by Shanghai PRET Bantai, detailing mechanical properties, processing parameters and applications.
The PPS 804 GM6 is a polyphenylene sulfide material offering good mechanical properties, dimensional stability, excellent molding performance and a natural surface appearance. It meets UL‑94 V0 flammability and is supplied for the Asia‑Pacific region.
Typical applications include automotive components and electrical/electronic parts, processed mainly by injection molding. The datasheet provides density, tensile strength, flexural properties, heat deflection temperature and recommended processing conditions such as drying and molding temperatures. This manual is written in Chinese.
| Density | 1.96 g/cm³ (23 °C) |
|---|---|
| Tensile Strength | 135 MPa (50 mm/min) |
| Elongation at Break | 1.3 % (50 mm/min) |
| Flexural Strength | 215 MPa (2 mm/min) |
| Flexural Modulus | 19 000 MPa (2 mm/min) |
| Heat Deflection Temperature | 260 °C (1.8 MPa, flat) |
| Flammability | UL 94 Class V0 (1.6 mm) |
| Mold Shrinkage | 0.2‑0.6 % (23 °C) |
| Drying Condition | 130 °C for 4‑6 h |
| Injection Temperature | 300‑330 °C (F), 295‑325 °C (M), 270‑300 °C (B) |
The density is 1.96 g/cm³ measured at 23 °C.
Injection temperatures should be set to 300‑330 °C for the F grade, 295‑325 °C for the M grade, or 270‑300 °C for the B grade.
Yes, it meets UL 94 Class V0 flammability rating.
It is used in automotive components and electrical/electronic applications.